Investigação comparativa das propriedades estruturais do diboreto de magnésio dopado com compostos de carbono

Página do item simplificado
dc.contributor.advisorSantos, Dayse Iara dos [UNESP]
dc.contributor.authorRocha, Alcir Laerte Tanck [UNESP]
dc.contributor.institutionUniversidade Estadual Paulista (Unesp)
dc.date.accessioned2014-06-11T19:23:26Z
dc.date.available2014-06-11T19:23:26Z
dc.date.issued2009-08-20
dc.description.abstractO intermetálico diboreto de magnésio passou a ser um material intensamente estudado a partir de 2001, quando nele encontrou-se a propriedade de supercondição de corrente elétrica. Embora sua transição seja em temperatura relativamente baixa, próximo de 40 K, é grande o interesse comercial neste material devido à provável simplicidade da cinética de reação e à maneira direta e barata de processamento. Partindo de pós precursores ultrafinos de boa qualidade a formação da fase Mg'B IND. 2' parece ocorrer em apenas alguns minutos em temperatura relativamente baixa (650ºC). Sob este ponto de vista, este material é considerado bastante atrativo comercialmente, quando comparado aos supercondutores cerâmicos cujo processamento é muito mais complexo. Entretanto, suas propriedades supercondutoras, assim como nas cerâmicas, dependem da sua microestrutura e, portanto da cinética de formação da fase supercondutora. Além disso, com o objetivo de ampliar a densidade de corrente elétrica sob campos magnéticos cada vez mais altos, tem-se utilizado artifícios tais como a adição de diversos compostos geradores de centros de aprisionamento de fluxo magnético. Entre eles figuram o SiC e o silicone, formados por elementos que podem substituir um dos átomos do composto supercondutor, ou que apenas geram defeitos intersticiais. Neste trabalho, investigou-se a influência das adições de alguns compostos de carbono na formação da fase Mg'B IND. 2', assim como a determinação de alguns aspectos das microestruturas obtidas. Estudou-se também as mudanças na cinética de formação da fase devido à diferente granulação do precursor de magnésio. Os dados obtidos por DRX, ATD/TG, BET e técnicas de medidas magnéticas indicaram que um novo composto testado (gasolina azul) poderá apresentar características vantajosas com relação a outras adições mais conhecidas.pt
dc.description.abstractThe intermetallic magnesium diboride has become the object of many studies since was found to be a superconducting material, at 2001. Although it shows relatively low critical temperature, it presents very interesting points, like the simplicity of the formation of a binary compound and non expensive precursors powders. Starting from ultrafine quality precursor powders the formation of Mg'B IND. 2' phase seems to occur in a few minutes at low temperature (650ºC), what is considered commercially quite attractive when compared to complicated ceramic superconductors. Nevertheless, its superconducting properties, as well as the ceramics, depend on its microsstructure and, consequently on the kinetics of formation of the superconducting phase. Besides that, with the aim of enlarging the critical current density under higher magnetic fields, the addition of several compounds has been used in order to generate pinning centers. Silicon carbide and silicon oil are cited among the most used additions, which act like substitutional or interstitial impurities and defects generators. In this work, the influence of the addition of a few carbon compounds on the Mg'B IND. 2' phase formation was investigated, as well as the determination of a few structural parameters of the obtained materials. It was also studied the changes in the phase formation kinetics due to different magnesium precursor granulation. The XRD, DTA/TGA and magnetic measurements results indicated that the addition of a new compound (petrol) may present advantages to the additions already found in literature.en
dc.format.extent96 f. : il.
dc.identifier.aleph000597668
dc.identifier.capes33004056083P7
dc.identifier.citationROCHA, Alcir Laerte Tanck. Investigação comparativa das propriedades estruturais do diboreto de magnésio dopado com compostos de carbono. 2009. 96 f. Dissertação (mestrado) - Universidade Estadual Paulista, Faculdade de Ciências, 2009.
dc.identifier.filerocha_alt_me_bauru.pdf
dc.identifier.lattes8506867595279427
dc.identifier.urihttp://hdl.handle.net/11449/88365
dc.language.isopor
dc.publisherUniversidade Estadual Paulista (Unesp)
dc.rights.accessRightsAcesso aberto
dc.sourceAleph
dc.subjectMicroestruturapt
dc.subjectIntermetálicopt
dc.subjectSupercondutorpt
dc.subjectMedidas magnéticaspt
dc.subjectSuperconductoren
dc.subjectMicrostructureen
dc.subjectMagnetic measurementsen
dc.titleInvestigação comparativa das propriedades estruturais do diboreto de magnésio dopado com compostos de carbonopt
dc.typeDissertação de mestrado
unesp.author.lattes8506867595279427
unesp.campusUniversidade Estadual Paulista (Unesp), Faculdade de Ciências, Baurupt
unesp.graduateProgramCiência e Tecnologia de Materiais - FCpt
unesp.knowledgeAreaCiência dos materiaispt

Arquivos

Pacote Original
Agora exibindo 1 - 1 de 1
Imagem de Miniatura
Nome:
rocha_alt_me_bauru.pdf
Tamanho:
1.83 MB
Formato:
Adobe Portable Document Format
Baixar

Coleções

Dissertações - Ciência e Tecnologia de Materiais - FC